Features of thermal decomposition of a new precursor for Mg–Zr mixed oxide preparation

Abstract

A new peroxo-method for Mg–Zr mixed oxide preparation has been applied. It has been established that this precursor after being heated up to 700 ºC is in the form of poorly crystalline Mg–Zr oxide. Thermal and X-ray diffractional analyses have shown that the oxide phase is formed directly from amorphous peroxocomplex, avoiding formation of intermediate Mg(OH)2 phase. The peroxocomplex-mediated route allows achieving high degree of molecular homogeneity in the mixed oxide and high distribution of the active sites due to its low crystallinity. The prepared material is a potential catalyst for aldol condensation reaction. Применён новый пероксо-метод получения смешанных оксидов Mg–Zr. Установлено, что исследованный прекурсор при нагревании до 700 ºC образует слабо-кристаллизованный оксид Mg–Zr. Методами термического анализа и рентгеновской дифракции показано, что оксидная фаза образуется непосредственно из аморфных пероксокомплексов без формирования промежуточной фазы Mg(OH)2. Пероксокомплексный путь позволяет достичь высокой степени молекулярной гомогенности в смешанных оксидах и высокого распределения активных центров за счёт низкой кристалличности материала. Полученные образцы являются потенциальными катализаторами для реакций альдольной конденсации.