Abstract:
The decomposition kinetics of austenite that appears in the 13KhFA low-alloyed pipe steel upon heating the samples in an intercritical temperature interval (ICI) and exposure for 5 or 30 min has been studied by the method of high-speed dilatometry. The results of dilatometry are supplemented by the microstructure analysis. Thermokinetic diagrams of the decomposition of the γ phase are represented. The conclusion has been drawn that an increase in the duration of exposure in the intercritical interval leads to a significant increase in the stability of the γ phase. © 2013 Pleiades Publishing, Ltd.