Calorimetric study of polyketone formed from carbon monoxide, ethylene and butene-1

Abstract

The temperature dependence of the heat capacity for partially crystalline polyketone derived from carbon monoxide with ethylene and butene-1 (the butane units content is 14.6 mol %) was studied over the range 6–520 K by the methods of precision adiabatic vacuum calorimetry and differential scanning calorimetry. Thermodynamic characteristics of the glass transition and glassy state and melting characteristics were determined. The standard thermodynamic functions, namely, С0р , H0 (T) - H0 (0), S0 (T) - S0 (0) and G0 (T) - H0 (0) , were calculated for the temperature range from T → 0 to 400 K, based on the experimental data. Thermal stability temperature for polyketone (520 K) has been specified by the thermogravimetry method. Методами прецизионной адиабатической и дифференциальной сканирующей калориметрии в интервале 6–520 K изучена температурная зависимость теплоемкости частично кристаллического поликетона, полученного на основе монооксида углерода с этиленом и бутеном-1 с содержанием бутановых звеньев 14,6 мол. %, определены его характеристики стеклования и стеклообразного состояния и термодинамические параметры плавления. По полученным экспериментальным данным рассчитаны стандартные термодинамические функции С0р, H0(T) - H0(0), S0(T) - S0(0) и G0(T) - H0(0) , для области от Т → 0 до 520 K. Методом термогравиметрии определена температура его термической устойчивости, проведены исследования по определению биоразлагаемости поликетона.